原料描述部分
| 规格级别 |
薄膜级 |
外观颜色 |
|
| 该料用途 |
用途：透明袋子,薄膜,汽车包装,重包装袋,收缩膜 |
| 备注说明 |
特性：透明度、张力及加工性良 |
②加工条件
③原料技术数据
| 性能项目 |
试验条件[状态] |
测试方法 |
测试数据 |
数据单位 |
| 基本性能 |
密度 |
|
ASTM D-1505 |
0.920 |
g/cm3 |
| 熔体流动速率 |
|
ASTM D-1238 |
3.0 |
g/10min |
| 机械性能 |
断裂伸长率 |
|
ASTM D-638 |
500 |
% |
| 破裂点张力 |
MD |
|
ASTM D-882 |
200 |
kg/cm2 |
| TD |
|
ASTM D-882 |
180 |
kg/cm2 |
| 抗撕裂张度 |
MD |
|
ASTM D-1922 |
300 |
g |
| TD |
|
ASTM D-1922 |
350 |
g |
| 屈服点张力 |
|
ASTM D-638 |
93 |
Kg/cm2 |
| 跌落冲击强度 |
|
ASTM D-1709 |
120 |
g |
| 断裂点伸张率 |
MD |
|
ASTM D-882 |
450 |
% |
| TD |
|
ASTM D-882 |
600 |
% |
| 抗张强度 |
|
ASTM D-638 |
120 |
Kg/cm2 |
| 热性能 |
低温脆化温度 |
|
ASTM D-746 |
<-76 |
°C |
| 维卡软化点 |
|
ASTM D-1525 |
90 |
°C |
|
|
|
|
|